FLEX – C 2 testing

High polymer modified, cement based, high strength, flexible tile adhesive , suitable for fully vitrified tiles & glass mosaics / blocks in interior & exterior situations specially for use on facades.

FLEX – C 1 is a cement based high Polymer modified tile adhesive for thin or thick bed fixing of all kind of tiles in interior or exterior situations. FLEX – C 1 is suitable for fixing materials such as fully vitrified tiles, Marble and Stone cladding.

FLEX – C 1 complies with the requirements of European Tile adhesive standards EN 12 004 i.e. C 1.

TYPICAL APPLICATIONS

FLEX – C 1 tile adhesive is suitable for variety of backgrounds / bases including concrete, cement / sand screeds and renders, concrete block wall and existing unglazed ceramic / vitrified tiles.
FLEX – C 1 may be used in areas where tiling is likely to be subjected to some limited background movement of vibration. It is especially suitable for fixing industrial tiles and other more special tiles and stones.

CHARACTERISTICS & ADVANTAGES

  • White and Grey 
  • Easy to use, just add water.
  • High bond strength
  • Water & Weather resistant.
  • Good flexibility , so it is suitable for use on facades
  • Good pot life.
  • Non toxic

SURFACE PREPARATION

The surface to be tiled should be sound, dimensionally stable, clean and free from dusty or friable materials, paint, grease, oil etc.

COVERAGE

  • Thin-bed fixing: 
    2 – 3kg/m² (Smooth surface using notched trowel)
  • Solid-bed fixing:
    5 – 6kg/m² (Smooth surface using notched trowel)

MIXING INSTRUCTIONS

Mix FLEX – C 1 slowly in clean and sweet water (approx. 4 – 5 liters) until a smooth & lump-free mixture is obtained.
Leave to stand for 15 minutes then stir. Don’t add further water.

APPLICATION INSTRUCTIONS

1- Apply FLEX – C 1 to a minimum depth of 3mm on a working area of not more than 1m². (See Note 1)

2- The adhesive bed should be combed horizontally with a notched trowel to remove excess.

3- Fix dry tiles by pressing into place with slight twisting motion (See Note 2)

4- Ensure that at least 65% of each tile is in contact with adhesive.

5- Clean off surplus adhesive from the face of the tile with a damp cloth. Similarly, joints must be raked out in readiness
for grouting.

6- Leave for a minimum of 24 hours before grouting.

Play Video

Note: 

1- Solid-bed fixing is recommended for wet conditions, Terrazzo and Marble flooring tiles and vertical heavy duty applications including decorative Stone cladding. But unlike the application of ordinary tiles, apply to the cladding itself and not to the substrate. For best results, allow no more then 35 kilos weight of stone cladding (of average thickness 10mm) per square meter.

2- Fix tiles (which should be dry) by pressing into place. Beginning at the bottom in the case of wall tiles and at center
markings in the case of floor and pool tiles.

WATCH POINTS

► FLEX C – 1 should not be used on painted or metal surfaces.
► The use of chilled water while mixing, will extend open wet time in high ambient temperatures.

WORKABILITY

Working time of FLEX C – 1 is about 45 minutes at 25°C, after 30 minutes standing time and tiles must be fixed in position before drying out occurs. For this reason, it is essential to work with in a comparatively small area at a time.

Colours

FLEX C – 1 is available in Grey & White Colours. 

Packaging

FLEX C – 1 is available in 20kg bags.

Storage

Store out of direct sunlight and protect from water.

PRECAUTIONS AND SAFETY MEASURES

This product contains Portland cement which is slightly alkaline when wet. For people with sensitive skin, continuous use may cause irritation. Gloves or a suitable barrier cream should be used. As a general Code of safety practice all chemical products should be treated with care, kept away from children and animals, especially protect eyes and skin. In emergency seek medical advice.

COMPOSITION, PROPERTIES, APPEARANCE

FLEX C – 1 is a blend of Portland cement, quartz sand, reinforced with polymer content & optimizing additives, for thin / thick bed performance.